Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
hakemus: Ship Plate
Special Steel: High-Strength Steel Plate
Tolerance: ±1%
Category: Ship Steel Plate, Hot Rolled Steel Sheet, Steel Plate
Processing Service: Punching, Decoiling, Welding, Bending, Cutting
| Myyntiyksiköt | : | Ton |
The file is encrypted. Please fill in the following information to continue accessing it
EH36 Laivanrakennusteräskemiallinen koostumus:
| Grade |
C max |
Si max |
Mn |
P max |
S max |
Als min |
Ti max |
Cu max |
Cr |
Ni |
Mo |
Nb |
V |
|
EH36 |
0.18 |
0.50 |
0.90-1.60 |
0.035 |
0.035 |
0.015 |
0.02 |
0.35 |
0.20 |
0.40 |
0.08 |
0.02-0.05 |
0.05-0.10 |
EH36 Meriteräslevy Mekninen ominaisuus:
|
Grade |
Rm |
Re(MPa) min |
A% min |
Akv/J min |
||||||
|
EH36 |
490-630 |
355 |
21 |
E.T °C |
Thickness (mm) |
|||||
|
-40 |
≤ 50 |
>50-70 |
>70-100 |
|||||||
|
L |
C |
L |
C |
L |
C |
|||||
|
34 |
24 |
41 |
27 |
50 |
34 |
|||||
FH36 Laivanrakennuslevyn kemiallinen koostumus:
| Grade |
C max |
Si max |
Mn |
P max |
S max |
Als min |
Ti max |
Cu max |
Cr |
Ni |
Mo |
Nb |
V |
N max |
|
FH36 |
0.16 |
0.50 |
0.90-1.60 |
0.025 |
0.025 |
0.015 |
0.02 |
0.35 |
0.20 |
0.80 |
0.08 |
0.02-0.05 |
0.05-0.10 |
0.009 |
FH36 Laivan rakennusteräslevy Mekninen omaisuus:
|
Grade |
Rm |
Re(MPa) min |
A% min |
Akv/J min |
||||||
|
FH36 |
490-630 |
355 |
21 |
E.T °C |
Thickness (mm) |
|||||
|
-60 |
≤ 50 |
>50-70 |
>70-100 |
|||||||
|
L |
C |
L |
C |
L |
C |
|||||
|
34 |
24 |
- |
- |
- |
- |
|||||
Ota meihin yhteyttä
Tietosuojalausunto: Yksityisyytesi on meille erittäin tärkeä. Yrityksemme lupaa olla paljastamatta henkilökohtaisia tietojasi mille tahansa laajentumiselle ilman nimenomaista käyttöoikeustasi.
Täytä lisätietoja, jotta voit ottaa sinuun yhteyttä nopeammin
Tietosuojalausunto: Yksityisyytesi on meille erittäin tärkeä. Yrityksemme lupaa olla paljastamatta henkilökohtaisia tietojasi mille tahansa laajentumiselle ilman nimenomaista käyttöoikeustasi.
Contact Now